Actual Certified Material Test Report
Alloy |
ER316 / 316L (AWS A5.9) |
Diameter |
5/32" |
Heat Number |
1T331 |
Date Entered |
8/19/2004 |
Entered By |
JLA |
CHEMICAL ANALYSIS: |
|
Carbon (C) |
0.0180 |
Chromium (Cr) |
18.7300 |
Cobalt (Co) |
0.2400 |
Copper (Cu) |
0.2500 |
Manganese (Mn) |
1.8500 |
Molybdenum (Mo) |
2.4100 |
Nickel (Ni) |
13.4000 |
Nitrogen (N) |
0.0340 |
Phosphorus (P) |
0.0200 |
Silicon (Si) |
0.5100 |
Sulfur (S) |
0.0120 |
Ferrite Schaeffler |
3.500 |
Ferrite Delong |
5.900 |
Ferrite WRC |
4.200 |
Typical Certified Material Test Report
Alloy |
ER316 / 316L (AWS A5.9) |
Date Entered |
9/10/2012 |
Entered By |
BY |
CHEMICAL ANALYSIS: |
|
Carbon (C) |
0.03 |
Chromium (Cr) |
18.0-20.0 |
Copper (Cu) |
0.75 |
Manganese (Mn) |
1.0-2.5 |
Molybdenum (Mo) |
2.0-3.0 |
Nickel (Ni) |
11.0-14.0 |
Phosphorus (P) |
0.03 |
Silicon (Si) |
0.30-0.65 |
Sulfur (S) |
0.03 |
YIELD STRENGTH, ksi: 58 |
|
TENSILE STRENGTH, ksi: 86 |
|
% ELONGATION min: 36 |