Actual Certified Material Test Report
Alloy |
ER316 / 316L (AWS A5.9) |
Diameter |
3/32" |
Heat Number |
1Y440 |
Date Entered |
8/10/2004 |
Entered By |
JLA |
CHEMICAL ANALYSIS: |
|
Carbon (C) |
0.0160 |
Chromium (Cr) |
18.6600 |
Copper (Cu) |
0.1500 |
Manganese (Mn) |
1.9300 |
Molybdenum (Mo) |
2.5700 |
Nickel (Ni) |
13.8100 |
Nitrogen (N) |
0.0320 |
Phosphorus (P) |
0.0240 |
Silicon (Si) |
0.4700 |
Sulfur (S) |
0.0130 |
Ferrite Schaeffler |
2.300 |
Ferrite Delong |
5.100 |
Ferrite WRC |
3.700 |
Typical Certified Material Test Report
Alloy |
ER316 / 316L (AWS A5.9) |
Date Entered |
9/10/2012 |
Entered By |
BY |
CHEMICAL ANALYSIS: |
|
Carbon (C) |
0.03 |
Chromium (Cr) |
18.0-20.0 |
Copper (Cu) |
0.75 |
Manganese (Mn) |
1.0-2.5 |
Molybdenum (Mo) |
2.0-3.0 |
Nickel (Ni) |
11.0-14.0 |
Phosphorus (P) |
0.03 |
Silicon (Si) |
0.30-0.65 |
Sulfur (S) |
0.03 |
YIELD STRENGTH, ksi: 58 |
|
TENSILE STRENGTH, ksi: 86 |
|
% ELONGATION min: 36 |