Actual Certified Material Test Report
Alloy |
ER309 / 309L (AWS A5.9) |
Diameter |
3/32" |
Heat Number |
PQ459 |
Date Entered |
1/7/2005 |
Entered By |
dbf |
CHEMICAL ANALYSIS: |
|
Aluminum (Al) |
0.0100 |
Carbon (C) |
0.0180 |
Chromium (Cr) |
23.5600 |
Cobalt (Co) |
0.0900 |
Copper (Cu) |
0.0900 |
Manganese (Mn) |
1.7000 |
Molybdenum (Mo) |
0.1000 |
Nickel (Ni) |
13.7600 |
Nitrogen (N) |
0.0560 |
Phosphorus (P) |
0.0180 |
Silicon (Si) |
0.4400 |
Sulfur (S) |
0.0050 |
Titanium (Ti) |
0.0070 |
Vanadium (V) |
0.1100 |
Ferrite Schaeffler |
8.600 |
Ferrite Delong |
12.700 |
Ferrite WRC |
10.500 |
CBTa |
0.0200 |
Typical Certified Material Test Report
Alloy |
ER309 / 309L (AWS A5.9) |
Date Entered |
8/7/2008 |
Entered By |
MJH |
CHEMICAL ANALYSIS: |
|
Carbon (C) |
0.03 |
Chromium (Cr) |
23.0-25.0 |
Copper (Cu) |
0.75 |
Manganese (Mn) |
1.0-2.5 |
Molybdenum (Mo) |
0.75 |
Nickel (Ni) |
12.0-14.0 |
Phosphorus (P) |
0.03 |
Silicon (Si) |
0.30-0.65 |
Sulfur (S) |
0.03 |
YIELD STRENGTH, PSI AS WELDED 58,000 |
|
TENSILE STRENGTH, PSI AS WELDED 85,000 |
|
% ELONGATION IN 2" AS WELDED 36 |