Actual Certified Material Test Report
Alloy |
ER316 / 316L (AWS A5.9) |
Diameter |
.035" |
Heat Number |
19898 |
Date Entered |
9/15/2004 |
Entered By |
JLA |
CHEMICAL ANALYSIS: |
|
Boron (B) |
0.0010 |
Carbon (C) |
0.0100 |
Chromium (Cr) |
18.320 |
Cobalt (Co) |
0.0700 |
Copper (Cu) |
0.080 |
Manganese (Mn) |
1.8800 |
Molybdenum (Mo) |
2.5300 |
Nickel (Ni) |
11.780 |
Niobium (Nb) |
0.0100 |
Nitrogen (N) |
0.0500 |
Phosphorus (P) |
0.0170 |
Silicon (Si) |
0.4200 |
Sulfur (S) |
0.0100 |
Vanadium (V) |
0.0500 |
Ferrite Schaeffler |
7.6 |
Ferrite Delong |
7.1 |
Ferrite WRC |
7.6 |
Typical Certified Material Test Report
Alloy |
ER316 / 316L (AWS A5.9) |
Date Entered |
9/10/2012 |
Entered By |
BY |
CHEMICAL ANALYSIS: |
|
Boron (B) |
|
Carbon (C) |
0.03 |
Chromium (Cr) |
18.0-20.0 |
Copper (Cu) |
0.75 |
Manganese (Mn) |
1.0-2.5 |
Molybdenum (Mo) |
2.0-3.0 |
Nickel (Ni) |
11.0-14.0 |
Phosphorus (P) |
0.03 |
Silicon (Si) |
0.30-0.65 |
Sulfur (S) |
0.03 |
YIELD STRENGTH, ksi: 58 |
|
TENSILE STRENGTH, ksi: 86 |
|
% ELONGATION min: 36 |