Actual Certified Material Test Report
Alloy |
ER309LSI (AWS A5.9) |
Diameter |
.023" |
Heat Number |
21652 |
Date Entered |
9/7/2004 |
Entered By |
JLA |
CHEMICAL ANALYSIS: |
|
Aluminum (Al) |
0.0100 |
Boron (B) |
0.0009 |
Carbon (C) |
0.0140 |
Chromium (Cr) |
23.000 |
Cobalt (Co) |
0.0800 |
Copper (Cu) |
0.0700 |
Manganese (Mn) |
1.9600 |
Molybdenum (Mo) |
0.1100 |
Nickel (Ni) |
14.000 |
Niobium (Nb) |
0.0100 |
Nitrogen (N) |
0.0550 |
Phosphorus (P) |
0.0170 |
Silicon (Si) |
0.7800 |
Sulfur (S) |
0.0010 |
Titanium (Ti) |
0.0100 |
Vanadium (V) |
0.1000 |
Ferrite Schaeffler |
7.7% |
Ferrite Delong |
10.2% |
Ferrite WRC |
8.0% |
Typical Certified Material Test Report
Alloy |
ER309LSI (AWS A5.9) |
Date Entered |
9/10/2012 |
Entered By |
BY |
CHEMICAL ANALYSIS: |
|
Boron (B) |
|
Carbon (C) |
0.03 |
Chromium (Cr) |
23.0-25.0 |
Copper (Cu) |
0.75 |
Manganese (Mn) |
1.0-2.5 |
Molybdenum (Mo) |
0.75 |
Nickel (Ni) |
12.0-14.0 |
Phosphorus (P) |
0.03 |
Silicon (Si) |
0.65-1.00 |
Sulfur (S) |
0.03 |
YIELD STRENGTH, ksi: 64 |
|
TENSILE STRENGTH, ksi: 87 |
|
% ELONGATION min: 41 |