Actual Certified Material Test Report
Alloy |
ER308 / 308L (AWS A5.9) |
Diameter |
1/8" |
Heat Number |
19047 |
Date Entered |
8/25/2004 |
Entered By |
JLA |
CHEMICAL ANALYSIS: |
|
Aluminum (Al) |
0.0040 |
Boron (B) |
0.0009 |
Carbon (C) |
0.0140 |
Chromium (Cr) |
19.600 |
Cobalt (Co) |
0.0700 |
Copper (Cu) |
0.0500 |
Manganese (Mn) |
1.9500 |
Molybdenum (Mo) |
0.0200 |
Nickel (Ni) |
10.080 |
Niobium (Nb) |
0.0100 |
Nitrogen (N) |
0.0540 |
Phosphorus (P) |
0.0160 |
Silicon (Si) |
0.4300 |
Sulfur (S) |
0.0110 |
Titanium (Ti) |
0.0100 |
Vanadium (V) |
0.1000 |
Ferrite Schaeffler |
8.8% |
Ferrite Delong |
7.0% |
Ferrite WRC |
8.4% |
Typical Certified Material Test Report
Alloy |
ER308 / 308L (AWS A5.9) |
Date Entered |
8/7/2008 |
Entered By |
MJH |
CHEMICAL ANALYSIS: |
|
Boron (B) |
|
Carbon (C) |
0.03 |
Chromium (Cr) |
19.5-22.0 |
Copper (Cu) |
0.75 |
Manganese (Mn) |
1.0-2.5 |
Molybdenum (Mo) |
0.75 |
Nickel (Ni) |
9.0-11.0 |
Phosphorus (P) |
0.03 |
Silicon (Si) |
0.30-0.65 |
Sulfur (S) |
0.03 |
YIELD STRENGTH, ksi AS WELDED: 54 |
|
TENSILE STRENGTH, ksi AS WELDED: 75 |
|
% ELONGATION IN 2" AS WELDED: 35 |