RBCuZn-D (Nickel Silver)
Alloy Type: A5.8, BRAZING Filler Metals
RBCuZn-D Nickel Silver (RBCuZn-D) is a bare or flux coated brazing rod used widely as a replacement for high cost silver brazing alloys when higher brazing temperatures are acceptable. The weld deposits have a very high tensile strength, good ductility and excellent corrosion resistance. Nickel Silver weld deposits are also readily machinable and will not work harden when put into service. A neutral or slightly oxidizing flame is recommended.
Typical Applications:
Brazing tungsten carbides, copper alloys, nickel alloys, stainless and carbon steel; building up and/or overlaying worn parts such as gear teeth, bearings, and valve seats; brazing steel or cast iron where good color match is desired
AWS Class: RBCuZn-D | Certification: AWS A5.8/A5.8M:2011 |
Alloy: RBCuZn-D | ASME SFA A5.8 |
Brazing Position: H, V | Brazing Range:
1720-1800⁰F |
Tensile Strength, kpsi: | 80-98 |
Elongation %, min: | 25 |
Melting Point | 1715⁰F | Solidification | 1690⁰F | Brinell Hardness | 90-110 |
Typical Wire Chemistry as per AWS A5.8 (single values are maximum)
Cu | Zn | Ni | P | Pb | Al | Si | Other |
46.0-50.0 | Rem | 9.0-11.0 | 0.25 | 0.05 | 0.01 | 0.04-0.25 | 0.50 |