Actual Certified Material Test Report
Alloy |
ECoCr-A (A5.13) |
Diameter |
3/32" |
Heat Number |
E000504 |
Date Entered |
3/30/2021 |
Entered By |
MH |
CHEMICAL ANALYSIS: |
|
Carbon (C) |
1.3 |
Chromium (Cr) |
27 |
Cobalt (Co) |
BAL |
Iron (Fe) |
3.4 |
Nickel (Ni) |
2.1 |
Phosphorus (P) |
0.009 |
Silicon (Si) |
1.1 |
Sulfur (S) |
0.02 |
Tungsten (W) |
5.0 |
Chemical Other |
0.1 |
ASME AWS/SFA-5.13 Specification |
Typical Certified Material Test Report
Alloy |
ECoCr-A (A5.13) |
Date Entered |
9/11/2012 |
Entered By |
BY |
CHEMICAL ANALYSIS: |
|
Carbon (C) |
0.7-1.4 |
Chromium (Cr) |
25.-32 |
Cobalt (Co) |
REM |
Iron (Fe) |
5.0 |
Manganese (Mn) |
2.0 |
Molybdenum (Mo) |
1.0 |
Nickel (Ni) |
3.0 |
Silicon (Si) |
2.0 |
Tungsten (W) |
3.0-6.0 |
Chemical Other |
1.0 |
YIELD STRENGTH, ksi: 101 TENSILE STRENGTH, ksi: 123 ELONGATION min: <1 |
|
HARDNESS: 36-45 HRC DENSITY: 0.305 IBS/ CU. IN |
|
MELTING RANGE: 2340-2570 DEGREES F |